Tribological behaviour of microalloyed Cu50Zr50 alloy

Abdurauf Younes, Silvia De la Flor, Stewart Clark, John Nutter, Martin Birkett, Joseph Watson, Matthew Unthank, Sergio Gonzalez Sanchez

Research output: Contribution to journalArticlepeer-review

Abstract

Promoting the martensitic transformation through optimum microalloying with Fe and/or Mn was observed to be an effective method to enhance the wear resistance of the Cu50Zr50 at. % shape memory alloy (SMA). Among all the potential microelements and concentrations, partial replacement of Cu by up to 1 at. % Fe and Mn is of interest since from density functional based calculations large minimization of the stacking fault energy (SFE) of the B2 CuZr phase is predicted. For this reason, an effective martensitic transformation is expected. The largest decrease of the SFE from 0.36 J/m2 to 0.26 J/m2 is achieved with partial replacement of Cu by 0.5 at. % Fe. This results in the highest martensitic transformation upon wear testing, especially at highest load (15 N) for which the mass loss is 0.0123 g compared to 0.0177 g for Cu50Zr50 and a specific wear rate of 5.9 mm3/Nm, compared to 8.5 for mm3/Nm for Cu50Zr50. This agrees with the low coefficient of friction of 0.48±0.05 and low roughness of 0.2000.013 μm of the Fe-containing alloy compared to that for Cu50Zr50, 0.55 and 0.4150.026 μm, respectively. All the worn surfaces show the formation of abrasive grooves, being shallowest for the more wear resistant 0.5 at. % Fe alloy. The second more wear resistant alloy contains 0.5 at. % Mn. Wear mechanisms of abrasion, adhesion and delamination have been identified.
Original languageEnglish
Article numberTRIB-21-1279
Pages (from-to)1-22
Number of pages22
JournalJournal of Tribology
Early online date7 Sep 2021
DOIs
Publication statusE-pub ahead of print - 7 Sep 2021

Fingerprint

Dive into the research topics of 'Tribological behaviour of microalloyed Cu50Zr50 alloy'. Together they form a unique fingerprint.

Cite this